Low MOQ for P91 Welding Filler Wire - JQ.MH00Cr24Ni13 stainless steel submerged-arc welding wire – Jinqiao

Send email to us

Product Detail

Product Tags

Feedback (2)

Our well-equipped facilities and great good quality regulate throughout all stages of manufacturing enables us to guarantee total buyer gratification for Wire Mesh 50x50, Welding Wire Types, Deformed Wire Mesh, We warmly welcome clients from all around the world for almost any sort of cooperation with us to build a mutual advantage potential. We've been devoting ourselves wholeheartedly to supply consumers the very best company.

Low MOQ for P91 Welding Filler Wire - JQ.MH00Cr24Ni13 stainless steel submerged-arc welding wire – Jinqiao Detail:

Features

Compared with manual welding, the deposition speed can be increased by 2-4 times, and the deposition efficiency is as high as 90%.

The adaptability of current and voltage is large, the setting of welding conditions is easy, and it is easy to carry out semi-automatic and automatic welding.

Good slag removal and glossy weld bead surface. In addition, there is little splash, the arc stability is excellent, and the X-ray is qualified.

Welding wire chemical composition(Wt%)

Model	Welding wire chemical composition（Wt%）
Model	C	Mn	Si	Cr	Ni	P	S	Cu	other
JQ.MH00Cr24Ni13	0.026	1.74	0.58	23.49	12.9	0.024	0.008	-	-

Product performance

Compliant (equivalent) standard model		An example of physical properties of deposited metal (with SJ601)
GB	AWS	Tensile StrengthMPa	Elongation%
F309L-H00Cr24Ni13	ER309L	558	40.0

Product welding reference current(AC or DC+)

Diameter(mm)	￠2.5	￠3.2	￠4.0	￠5.0
Welding current(A)	400-500	450-550	500-600	550-650

Product Specifications

Wire diameter	￠2.5	￠3.2	￠4.0	￠5.0
Package weight	25/50/100/200/250/300/350Kg/piece

Precautions for product use

1. The temperature between welds is recommended to be controlled at about 150°C. When multi-pass multi-layer welding of small and medium-sized specifications, pay attention to controlling the welding line energy.
2. The rust layer, moisture, oil, dust, etc. of the welding part must be cleaned up.
3. The flux must be baked at 300-350℃ for 2h before use.
The above suggestions are for reference only, and the actual situation shall prevail in the specific operation. If necessary, process qualification should be carried out before determining the welding plan.

Product detail pictures:

Related Product Guide:

We are proud of the superior customer gratification and wide acceptance due to our persistent pursuit of top of the range both of those on merchandise and service for Low MOQ for P91 Welding Filler Wire - JQ.MH00Cr24Ni13 stainless steel submerged-arc welding wire – Jinqiao , The product will supply to all over the world, such as: Croatia, Slovenia, Egypt, Our team knows well the market demands in different countries, and is capable of supplying suitable quality products and solutions at the best prices to different markets. Our company has already set up a experienced, creative and responsible team to develop clients with the multi-win principle.